Objective To prepare silver-containing hydroxyapatite coating (hydroxyapatite/Ag, HA/Ag) and investigate its antibacterial property and biocompatibil ity in vitro. Methods Vacuum plasma spraying technique was adopted to prepare HA/Ag coating on titanium alloy substrate (3% Ag). After incubating the HA/Ag and the HA coating under staphylococcus aureus and pseudomonas aeruginosa suspensions of 2% tryptic soy broth (TBS) medium for 2, 4 and 7 days, respectively, the biofilm on the coatings was examined by confocal laser scanning microscope, and the bacterial density and viable bacterial percentage of bacterial biofilm were calculated. Meanwhile, the micro-morphology of bacterial biofilm was observed by SEM, the cytotoxicity was detected via MTT and the biocompatibil ity of biofilm was evaluated by acute aemolysis test. Results Compared with HA coating, the bacterial biofilm’s thickness on the surface of HA/Ag coating witnessed no significant difference at 2 days after culture (Pgt; 0.05), but decreased obviously at 4 and 7 days after culture (P lt; 0.01). The bacterial density of the biofilm increased with time, but there was no significant difference between two coatings (P gt; 0.05) at 2, 4 and 7 days after culture. The viable bacterial percentage of the biofilms on the surface of HA/Ag coating decreased obviously compared with that of HA coating at 2, 4 and 7 days after cultureP lt; 0.01). The MTT notified the cytotoxic grade of both coatings was zero. The acute haemolysis assay showed that the hemolytic rate of HA/Ag and HA coating was 0.19% and 0.12%, respectively. Conclusion With good biocompatibil ity, significant antibacterial property against staphylococcus aureus and pseudomonas aeruginosa, no obvious cytotoxicity and no erythrocyte destruction, the vacuum plasma sprayed HA/Ag coating is a promising candidate for the surface of orthopedic metal implants to improve their osseointegration and antibacterial property.
ObjectiveTo review antibacterial/osteogenesis dual-functional surface modification strategy of titanium-based implants, so as to provide reference for subsequent research. MethodsThe related research literature on antibacterial/osteogenesis dual-functional surface modification strategy of titanium-based implants in recent years was reviewed, and the research progress was summarized based on different kinds of antibacterial substances and osteogenic active substances. ResultsAt present, the antibacterial/osteogenesis dual-functional surface modification strategy of titanium-based implants includes: ① Combined coating strategy of antibiotics and osteogenic active substances. It is characterized in that antibiotics can be directly released around titanium-based implants, which can improve the bioavailability of drugs and reduce systemic toxicity. ② Combined coating strategy of antimicrobial peptides and osteogenic active substances. The antibacterial peptides have a wide antibacterial spectrum, and bacteria are not easy to produce drug resistance to them. ③ Combined coating strategy of inorganic antibacterial agent and osteogenic active substances. Metal ions or metal nanoparticles antibacterial agents have broad-spectrum antibacterial properties and various antibacterial mechanisms, but their high-dose application usually has cytotoxicity, so they are often combined with substances that osteogenic activity to reduce or eliminate cytotoxicity. In addition, inorganic coatings such as silicon nitride, calcium silicate, and graphene also have good antibacterial and osteogenic properties. ④ Combined coating strategy of metal organic frameworks/osteogenic active substances. The high specific surface area and porosity of metal organic frameworks can effectively package and transport antibacterial substances and bioactive molecules. ⑤ Combined coating strategy of organic substances/osteogenic active substancecs. Quaternary ammonium compounds, polyethylene glycol, N-haloamine, and other organic compounds have good antibacterial properties, and are often combined with hydroxyapatite and other substances that osteogenic activity. ConclusionThe factors that affect the antibacterial and osteogenesis properties of titanium-based implants mainly include the structure and types of antibacterial substances, the structure and types of osteogenesis substances, and the coating process. At present, there is a lack of clinical verification of various strategies for antibacterial/osteogenesis dual-functional surface modification of titanium-based implants. The optimal combination, ratio, dose-effect mechanism, and corresponding coating preparation process of antibacterial substances and bone-active substances are needed to be constantly studied and improved.
Compound Huangbai liquid coating agent is a preparation that combines multiple traditional Chinese medicinal herbs and has shown significant efficacy in burn treatment. In recent years, the application of this coating agent in burn treatment has received widespread attention, and it plays a role in promoting wound healing, preventing infection, and reducing patient pain. This article reviews the research progress of compound Huangbai liquid coating agent in burn treatment, explores its mechanism of promoting wound healing, evaluates its current advantages and limitations in burn treatment, and provides scientific basis and theoretical support for its better use in burn treatment.
Objective To investigate the antibacterial and osteogenic capabil ities in vivo of hydroxyapatite (HA)/silver (Ag) coating. Methods HA/Ag coating (Ag qual ity percentage was 3%) and HA coating were deposited to external fixator Schanz screws. The tibial fracture model was establ ished in right hindl imb of 18 adult male Beagle dogs (weighing 15-20 kg). Thetibia was stabil ized with an external fixator and 2 Schanz screws of HA coating at proximal tibia (control group, n=18) and HA/Ag coating at distal tibia (experimental group, n=18), and every screw incision was infected with Staphylococcus aureus. Infection in screw holes and the changes of bone-screw interface were observed by wound grading and X-ray films. Results In control group, wounds infection became worse with time (χ2=13.492, P=0.001), while in experimental group, no obvious change was observed (χ2=0.208, P=0.901). The wound grading of experimental group was significantly better than that of the control group at 1, 2, and 3 weeks (P lt; 0.05). Laser scanning confocal microscope showed that there was bacterial adhesion on the surface of screws in 2 groups, viable becteria mainly in control group and non-viable becteria mainly in experimental group. The scanning electron microscope (SEM) observation results of the fractured sclerous tissue section showed that an obvious transparent boundary between screw and bone in control group, but no obvious boundary in experimental group. The osseointegration ratios were 76.23% ± 15.54% in control group and 93.42% ± 5.53% in experimental group, showing significant difference (t=8.843, P=0.000). The SEM observation showed that HA/Ag coating integrated with new bone and the surface of implant was filled with new bone in experimental group; obvious interspace was seen between the HA coating and new bone in control group. Conclusion HA/Ag coating has good antibacterial and osteogenic capabil ities, so it can take effects in preventing infection in screw holes and loosening of implants.
ObjectiveTo review the research progress of cementless intercalary prosthesis stem. MethodsThe literature about the cementless intercalary prosthesis in treatment of bone defects of extremities was reviewed, and the designing and application of prosthesis stem were analyzed. ResultsCementless intercalary prosthesis has the advantages of good biocompatibility. However, there are also some disadvantages, including the multiple factors affecting the fixation of the prosthesis stem and individual differences in the stability of the prosthesis. The methods to improve the fixation stability of prosthesis stem mainly include the optimization of prosthesis stem shape, addition of auxiliary fixation, and improvement of coating materials on the stem surface as well as porous structure of the stem surface. Among these methods, augment with auxiliary fixation has the most satisfactory effect on improving the stability of prosthesis. However, the deficiency of the method is the increasing risk of the larger incision exposure and surgical trauma. ConclusionImproving the design and fixation method of the cementless intercalary prosthesis stem can further improve the stability of the prosthesis. Under the premise of avoiding increasing surgical trauma as much as possible, addition of the auxiliary fixation can be a feasible choice to improve the fixation stability of prosthesis.
Objective To understand the value of pre-coating in artificial vessel endothelialization. Methods Literature concerning precoating in artificial vessel endothelialization was extensively reviewed. Results Pre-coating included chemical coatings(collagen, fibronectin, laminin, poly-l-lysin, gelatin andextracellular matrix), pre-clotting(plasma, blood, serum and fibrin glue), chemical bonding (heparin, RGD and lectins) and surface modification. Most of them could enhance the adhesion of the endothelial cells. Conclusion Pre-coating couldimprove endothelialization, but further research is needed to search for the appropriate concentration and incubation time.
Objective To design and construct a graphene oxide (GO)/silver nitrate (Ag3PO4)/chitosan (CS) composite coating for rapidly killing bacteria and preventing postoperative infection in implant surgery. Methods GO/Ag3PO4 composites were prepared by ion exchange method, and CS and GO/Ag3PO4 composites were deposited on medical titanium (Ti) sheets successively. The morphology, physical image, photothermal and photocatalytic ability, antibacterial ability, and adhesion to the matrix of the materials were characterized. Results The GO/Ag3PO4 composites were successfully prepared by ion exchange method and the heterogeneous structure of GO/Ag3PO4 was proved by morphology phase test. The heterogeneous structure formed by Ag3PO4 and GO reduced the band gap from 1.79 eV to 1.39 eV which could be excited by 808 nm near-infrared light. The photothermal and photocatalytic experiments proved that the GO/Ag3PO4/CS coating had excellent photothermal and photodynamic properties. In vitro antibacterial experiments showed that the antibacterial rate of the GO/Ag3PO4/CS composite coating against Staphylococcus aureus reached 99.81% after 20 minutes irradiation with 808 nm near-infrared light. At the same time, the composite coating had excellent light stability, which could provide stable and sustained antibacterial effect. ConclusionGO/Ag3PO4/CS coating can be excited by 808 nm near infrared light to produce reactive oxygen species, which has excellent antibacterial activity under light.
Objective To research in vitro biocompatibility of silicon containing micro-arc oxidation (MAO) coated magnesium alloy ZK60 with osteoblasts. Methods The surface microstructure of silicon containing MAO coated magnesium alloy ZK60 was observed by a scanning electron microscopy (SEM), and chemical composition of the coating surface was determined by energy dispersive spectrum analysis. The experiments were divided into 4 groups: silicon containing MAO coated magnesium alloy ZK60 group (group A), uncoated magnesium alloy ZK60 group (group B), titanium alloy group (group C), and negative control group (group D). Extracts were prepared respectively with the surface area to extraction medium ratio (1.25 cm2/ mL) according to ISO 10993-12 standard in groups A, B, and C, and were used to culture osteoblasts MC3T3-E1. The α-MEM medium supplemented with 10% fetal bovine serum was used as negative control in group D. The cell morphology was observed by inverted phase contrast microscopy. MTT assay was used to determine the cell viability. The activity of alkaline phosphatase (ALP) was detected. Cell attachment morphology on the surface of different samples was observed by SEM. The capability of protein adsorption of the coating surface was assayed, then DAPI and calcein-AM/ethidium homodimer 1 (calcein-AM/EthD-1) staining were carried out to observe cell adhesion and growth status. Results The surface characterization showed a rough and porous layer with major composition of Mg, O, and Si on the surface of silicon containing MAO coated magnesium alloy ZK60 by SEM. After cultured with the extract, cells grew well and presented good shape in all groups by inverted phase contrast microscopy, group A was even better than the other groups. At 5 days, MTT assay showed that group A presented a higher cell proliferation than the other groups (P lt; 0.05). Osteoblasts in groups A and C presented a better cell extension than group B under SEM, and group A exhibited better cell adhesion and affinity. Protein adsorption in group A [ (152.7 ± 6.3) μg/mL] was significantly higher than that of group B [(96.3 ± 3.9) μg/mL] and group C [ (96.1 ± 8.7) μg/mL] (P lt; 0.05). At each time point, the adherent cells on the sample surface of group A were significantly more than those of groups B and C (P lt; 0.05). The calcein-AM/EthD-1 staining showed that groups A and C presented better cell adhesion and growth status than group B. The ALP activities in groups A and B were 15.55 ± 0.29 and 13.75 ± 0.44 respectively, which were significantly higher than those in group C (10.43 ± 0.79) and group D (10.73 ± 0.47) (P lt; 0.05), and group A was significantly higher than group B (P lt; 0.05). Conclusion The silicon containing MAO coated magnesium alloy ZK60 has obvious promoting effects on the proliferation, adhesion, and differentiation of osteoblasts, showing a good biocompatibility, so it might be an ideal surface modification method on magnesium alloys.
Implantation of drug-eluting stents (DES) is one of the most effective treatment for intraluminal vascular diseases such as vascular stenosis caused by atherosclerosis. Antiproliferative drugs offered by could significantly reduce the restenosis of blood vessels, which is beneficial to interventional therapy in more advanced and complex vascular diseases. This review sumarizes the state-of-the-art of the DES based on the function of loaded drug and material of the stents. We hope this review can provide basic information of DES for clinicians and researchers to make more rational choices in practical applications. Moreover, this review also propses the prospects of drug-loaded stents.
ObjectiveTo review the current research and application progress of three-dimentional (3D) printed porous titanium alloy after tumor resection, and provide direction and reference for the follow-up clinical application and basic research of 3D printed porous titanium alloy. MethodsThe related literature on research and application of 3D printed porous titanium alloy after tumor resection in recent years was reviewed from three aspects: performance of simple 3D printed porous titanium alloy, application analysis of simple 3D printed porous titanium alloy after tumor resection, and research progress of anti-tumor 3D printed porous titanium alloy. Results3D printing technology can adjust the pore parameters of porous titanium alloy, so that it has the same biomechanical properties as bone. Appropriate pore parameters are conducive to inducing bone growth, promoting the recovery of skeletal system and related functions, and improving the quality of life of patients after operation. Simple 3D printed porous titanium alloy can more accurately match the bone defect after tumor resection through preoperative personalized design, so that it can closely fit the surgical margin after tumor resection, and improve the accuracy and efficiency of the operation. The early and mid-term follow-up results show that its application reduces the postoperative complications such as implant loosening, subsidence, fracture and so on, and enhances the bone stability. The anti-tumor performance of 3D printed porous titanium alloy mainly includes coating and drug-loading treatment of pure 3D printed porous titanium alloy, and some progress has been made in the basic research stage. ConclusionSimple 3D printed porous titanium alloy is suitable for patients with large and complex bone defects after tumor resection, and the anti-tumor effect of 3D printed porous titanium alloy can be achieved through coating and drug delivery.